Heat Shrink Tubes With Low Temp 90℃, Shrinkage2:1
Caution
Product Description
This is an economy item, The price is cheaper than the MISUMI standard product.
[Features]
The outer layer of the shrink tube is made of soft polyolefin.
Shrinks quickly at temperatures as low as 90°C.
Shrink tubing designed to protect wiring harnesses. electronic components and other uses
Shrinkage ratio 2:1 to less than 3:1
Operating temperature range -55-125°C
Economy Low Temperature Heat Shrink Tube
- Low Shrinkage Temperature: Shrinks rapidly at just -90°C, reducing heat-related damage to components.
- Specific Shrink Ratio: Offers flexibility in application and space savings.
- Excellent Electrical Properties: High dielectric strength and volume resistivity for insulation protection.
- Cable gland with multiple size options
- Fast Installation: Rapid shrinkage reduces application time.
MISUMI Standard
Cheaper Price
Product Variety
3D CAD Support
Product of heat shrink tube Overview
● The heat shrink tube outer layer is made of soft polyolefin● Fast heat shrink tube at low temperature of 90 ℃
● Designed for wire harness protection, electronic component protection and other occasions requiring low-temperature shrinkage, to reduce the impact of high-temperature heating on devices during installation
● 14 models are available to provide a wide range of choices
*Note: each roll of heat shrink tube may have 1 to 3 adapters, which conforms to the industry standard and does not affect the quality. Please feel free to use.
Product of heat shrink tube Feature
Dimensional heat shrink tube Drawing
| Before heat shrink tube (mm) | After heat shrink tube (mm) | |||||||||||||||
| Part number | Inner Diameter D | Wall Thickness H | Maximum Inner Diameter d | Wall Thickness h | ||||||||||||
| MTUBE-DW-1 | 1.5±0.3 | 0.20±0.05 | 0.60 | 0.33±0.06 | ||||||||||||
| MTUBE-DW-2 | 2.5±0.3 | 0.20±0.05 | 1.00 | 0.44±0.06 | ||||||||||||
| MTUBE-DW-3 | 3.5±0.3 | 0.25±0.05 | 1.50 | 0.44±0.06 | ||||||||||||
| MTUBE-DW-4 | 4.5±0.3 | 0.25±0.05 | 2.00 | 0.44±0.06 | ||||||||||||
| MTUBE-DW-5 | 5.5±0.3 | 0.28±0.05 | 2.50 | 0.56±0.06 | ||||||||||||
| MTUBE-DW-6 | 6.5±0.3 | 0.28±0.05 | 3.00 | 0.56±0.06 | ||||||||||||
| MTUBE-DW-7 | 7.6±0.3 | 0.30±0.07 | 3.50 | 0.56±0.07 | ||||||||||||
| MTUBE-DW-8 | 8.6±0.3 | 0.30±0.07 | 4.00 | 0.56±0.07 | ||||||||||||
| MTUBE-DW-9 | 9.6±0.3 | 0.30±0.07 | 4.50 | 0.56±0.07 | ||||||||||||
| MTUBE-DW-10 | 10.7±0.4 | 0.30±0.07 | 5.00 | 0.56±0.07 | ||||||||||||
| MTUBE-DW-11 | 11.7±0.4 | 0.30±0.07 | 5.50 | 0.56±0.07 | ||||||||||||
| MTUBE-DW-12 | 12.7±0.4 | 0.30±0.07 | 6.00 | 0.56±0.07 | ||||||||||||
| MTUBE-DW-15 | 15.7±0.5 | 0.35±0.08 | 7.50 | 0.69±0.08 | ||||||||||||
| MTUBE-DW-20 | 21.0±0.5 | 0.40±0.10 | 10.00 | 0.77±0.10 | ||||||||||||
Specifications of heat shrink tube Overview
| heat shrink tube Material | heat shrink tube Polyolefin | ||||||||
| Shrinkage Ratio | 2:1 | ||||||||
| Operating Temperature Range | -55-125℃ | ||||||||
| Initial Shrinkage Temperature | 70℃ | ||||||||
| Minimum Complete Shrinkage Temperature | 90℃ (30 seconds) |
| heat shrink tube Item | Indicator Requirements | heat shrink tube Test Method | Typical Value | ||||||||||||||||
| Longitudinal Shrinkage Rate (200±5 ℃ for 3 minutes) | ±10% | ASTM D 2671 | ±7% | ||||||||||||||||
| Tensile Strength | ≥9.0MPa | ASTM D 638 | 10 Mpa | ||||||||||||||||
| Breakage Elongation | ≥250% | ASTM D 638 | 500% | ||||||||||||||||
| Breakage Elongation After Aging (Thermal aging for 168 hours at 158℃) | ≥100% | ASTM D 638 | 300% | ||||||||||||||||
| Thermal Shock (200±5 ℃ for 4 hours) | The outer layer is crack free, trickling free and dripping free | ASTM D 2671 | pass | ||||||||||||||||
| Low Temperature Flexibility (4 hours at -55 ℃) | Crack Free | ASTM D 2671 | pass | ||||||||||||||||
| Dielectric Strength and Breakdown | 2500V, 60sec, no breakdown | ASTM D 2671 | pass | ||||||||||||||||
| Volume Resistivity | ≥1012Ω·cm min. | ASTM D 876 | 1014Ω·cm | ||||||||||||||||
| Copper Corrosion (121±2℃ for 16 hours) | No Corrosion | ASTM D 2671 | pass | ||||||||||||||||
| Copper Stability (168 hours at 158 ℃) | Elongation≥100% | ASTM D 2671 | pass |